Arsenic (As) is among the most dangerous metalloids and is harmful to human wellbeing. In this laboratory study, Al(III)-modified kapok fibres (Al-Kapok) were used to remove As(V) from water. The sorbent was characterised using Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) combined with energy-dispersive X-ray spectroscopy (EDX). Batch experiments were performed to observe the performance of Al-Kapok in the removal of As(V) and to examine the effects of pH, temperature, adsorbent dose, and coexisting ions on the adsorption process. The surface of the sorbent changed after aluminium modification, and the results of the batch experiments showed that the adsorption of As(V) occurred mainly via endothermic-spontaneous chemisorption at the solution and solid interface of Al-Kapok. The As(V) removal efficiency was approximately 76%-84%, and it was slightly affected at pH levels below 8.0. Further study showed that the maximum adsorption capacity of Al-Kapok for As(V) was 118 μg/g at 30 °C and pH 6, and notable adverse effects were caused by the presence of SO42-and PO43-. It was also found that the boundary layer and film diffusion contributed more to As(V) adsorption. After five adsorption/desorption cycles, regeneration recovered approximately 92% of the adsorption capacity of Al-Kapok used. Overall, Al-Kapok appears to be a suitable adsorbent material for the purification of As-contaminated water.
Keywords: Aluminium; Arsenic adsorption; Kapok fibres; Natural adsorbent.
Copyright © 2022 Elsevier Ltd. All rights reserved.