Although N-heterocyclic carbenes (NHCs) are superior to thiol adsorbates in that they form remarkably stable bonds with gold, the generation of NHC-based self-assembled monolayers (SAMs) typically requires a strong base and an inert atmosphere, which limits the utility of such films in many applications. Herein, we report the development and use of bench-stable NHC adsorbates, benzimidazolium methanesulfonates, for the direct formation of NHC films on gold surfaces under an ambient atmosphere at room temperature without the need for extraordinary precautions. The generated NHC SAMs were fully characterized using ellipsometry, X-ray photoelectron spectroscopy (XPS), polarization modulation infrared reflection-absorption spectroscopy (PM-IRRAS), and contact angle measurements, and they were compared to analogous SAMs generated from an NHC bicarbonate adsorbate. Based on these findings, a unique radical initiator α,ω-bidentate azo-terminated NHC adsorbate, NHC15AZO[OMs], was designed and synthesized for the preparation of SAMs on gold surfaces with both NHC headgroups bound to the surface. The adsorbate molecules in NHC15AZO SAMs can exist in a hairpin or a linear conformation depending on the concentration of the adsorbate solution used to prepare the SAM. These conformations were studied by a combination of ellipsometry, XPS, PM-IRRAS, and scanning electron microscopy using gold nanoparticles (AuNPs) as a tag material. Moreover, the potential utility of these unique radical-initiating NHC films as surface-initiated polymerization platforms was demonstrated by controlling the thickness of polystyrene brush films grown from azo-terminated NHC monolayer surfaces simply by adjusting the reaction time of the photoinitiated radical polymer growth process.
Keywords: N-heterocyclic carbenes (NHCs); azo surface initiator; benzimidazolium methanesulfonates; photoinitiated radical polymerization; polymer brushes; self-assembled monolayers (SAMs); surface-initiated polymerization; thickness control.