This paper presents the use of hydrophobic silica aerogel (HSA) and hydrophilic fly ash cenosphere (FCS) aggregates for improvements in the thermal insulating and mechanical properties of 100- and 250 °C-autoclaved calcium aluminate phosphate (CaP) cement composites reinforced with micro-glass (MGF) and micro-carbon (MCF) fibers for deployment in medium- (100 °C) and high-temperature (250 °C) reservoir thermal energy storage systems. The following six factors were assessed: (1) Hydrothermal stability of HSA; (2) Pozzolanic activity of the two aggregates and MGF in an alkali cement environment; (3) CaP cement slurry heat release during hydration and chemical reactions; (4) Composite phase compositions and phase transitions; (5) Mechanical behavior; (6) Thermal shock (TS) resistance at temperature gradients of 150 and 225 °C. The results showed that hydrophobic trimethylsilyl groups in trimethylsiloxy-linked silica aerogel structure were susceptible to hydrothermal degradation at 250 °C. This degradation was followed by pozzolanic reactions (PR) of HSA, its dissolution, and the formation of a porous microstructure that caused a major loss in the compressive strength of the composites at 250 °C. The pozzolanic activities of FCS and MGF were moderate, and they offered improved interfacial bonding at cement-FCS and cement-MGF joints through a bridging effect by PR products. Despite the PR of MGF, both MGF and MCF played an essential role in minimizing the considerable losses in compressive strength, particularly in toughness, engendered by incorporating weak HSA. As a result, a FCS/HSA ratio of 90/10 in the CaP composite system was identified as the most effective hybrid insulating aggregate composition, with a persistent compressive strength of more than 7 MPa after three TS tests at a 150 °C temperature gradient. This composite displayed thermal conductivity of 0.28 and 0.35 W/mK after TS with 225 and 150 °C thermal gradients, respectively. These values, below the TC of water (TC water = 0.6 W/mK), were measured under water-saturated conditions for applications in underground reservoirs. However, considering the hydrothermal disintegration of HSA at 250 °C, these CaP composites have potential applications for use in thermally insulating, thermal shock-resistant well cement in a mid-temperature range (100 to 175 °C) reservoir thermal energy storage system.
Keywords: calcium phosphate cement; geothermal cement; hydrophobic cement; lightweight cement; reservoir thermal energy storage; silica aerogel; thermal-shock-resistant cement; thermally insulating cement.