To alleviate the safety hazards associated with the use of epoxy resin (EP), a multifunctional filler was designed. This study firstly combines the superior mechanical properties of magnesium borate rods (MBR) with the excellent smoke suppression and flame-retardant characteristics of layered double hydroxide (LDH). H2PO4- intercalated LDH (LDHP) was coated on the MBR surface to obtain inorganic composite particles MBR@LDHP. Subsequently, MBR@LDHP was modified with 3-aminopropyltriethoxysilane (APES) to obtain organic-inorganic composite particles MBR@LDHP-APES. Eventually, the hybrid particles were added to EP to prepare the composite materials. Thereafter, the morphology, composition, and structure of MBR@LDHP-APES were characterized utilizing scanning electron microscopy (SEM), Fourier transform infrared (FTIR), and X-ray diffraction (XRD). The results indicated the successful preparation of MBR@LDHP-APES, after which we investigated the effects of MBR@LDHP-APES on the smoke suppression, flame retardancy, and mechanical characteristics of EP. As observed, the EP composites containing 7.5 wt% MBR@LDHP-APES exhibited superior smoke suppression and flame retardancy abilities. The limiting oxygen index reached 33.5%, which is 36.73% greater than pure EP, and the lowest values of total heat and smoke release were observed for the composite materials. In addition, the mechanical properties test revealed that MBR@LDHP-APES considerably enhanced the tensile strength as well as the flexural strength of the composites. Furthermore, mechanistic studies suggested that the barrier effect of MBR, endothermic decomposition of LDHP, and the synergistic effect of LDHP and APES contributed essentially to the smoke suppression and flame-retardant properties of the material. The findings of this research point to a potential method for enhancing the EP's ability to suppress smoke and flames while enhancing its mechanical properties.
Keywords: composites; epoxy resin; flame retardant; layered double hydroxide; magnesium borate rod.