Glycero-(9,10-trioxolane)-trioleate (ozonide of oleic acid triglyceride, OTOA) was introduced into polylactic acid (PLA) films in amounts of 5, 10, 30, 50, and 70% w/w. The morphological, mechanical, thermal, and water absorption properties of PLA films after the OTOA addition were studied. The morphological analysis of the films showed that the addition of OTOA increased the diameter of PLA spherulites and, as a consequence, increased the proportion of amorphous regions in PLA films. A study of the thermodynamic properties of PLA films by differential scanning calorimetry (DSC) demonstrated a decrease in the glass transition temperature of the films with an increase in the OTOA content. According to DSC and XRD data, the degree of crystallinity of the PLA films showed a tendency to decrease with an increase in the OTOA content in the films, which could be accounted for the plasticizing effect of OTOA. The PLA film with 10% OTOA content was characterized by good smoothness, hydrophobicity, and optimal mechanical properties. Thus, while maintaining high tensile strength of 21 MPa, PLA film with 10% OTOA showed increased elasticity with 26% relative elongation at break, as compared to the 2.7% relative elongation for pristine PLA material. In addition, DMA method showed that PLA film with 10% OTOA exhibits increased strength characteristics in the dynamic load mode. The resulting film materials based on optimized PLA/OTOA compositions could be used in various packaging and biomedical applications.
Keywords: biocompatibility; ozonide; polylactic acid; polymer films; trioleate.