The analyzed topic refers to the corrosion resistance and changes in microhardness of the heat-treated (HT) hot-dip zinc coating deposited on bolts. The research aimed to evaluate the influence of the HT on the increase of the coating hardness and changes in anticorrosion properties. Hot-dip zinc coating was deposited in industrial conditions (acc. EN ISO 10684) on chosen bolts (M12x60). The achieved results were assessed based on corrosion resistance tests in neutral salt spray (salt chamber) and microhardness measurements. Tests were conducted in accordance with the adopted fractional plan, generated in the DOE module of the Statistica software. Using the conjugate gradient method optimal parameters of HT were determined. The conducted tests proved that the controlled heat treatment may increase the hardness of the hot-dip zinc coating without a significant deterioration in its basic protective function (corrosion resistance). The observed changes in the hardness and corrosion resistance of the zinc coating are a consequence of changes in its structure.
Keywords: coating hardness; corrosion resistance; heat treatment; hot-dip zinc galvanizing.