The safety and stability of power systems are seriously threatened by the decay-like fracture of composite insulators. This paper analyzes the aging characteristics (physical properties, NMR, and FTIR) of the silicone rubber sheds of the decay-like fractured insulator. The same V-string insulator and a new insulator are used for comparison. The study shows that the sheds' degradation is concentrated on the side with heavy pollution. The physical properties (appearance, pollution, hardness, and hydrophobicity) of the high voltage end decrease significantly compared to other positions, but there is no direct connection between the physical properties of sheds and the decay-like fracture of the core rod. The severity of aging increases with a decrease in the equivalent transverse relaxation time T2. The main chain of the PDMS material was severely damaged at the location of the insulator fracture. NMR and FTIR can well judge the aging degree of silicone rubber housings. However, no definite characteristic quantity can characterize the decay-like fracture. It is challenging to evaluate the decay-like fracture of the silicone rubber shed only by its aging degree.
Keywords: aging; composite insulator; decay-like fracture; silicone rubber shed.