The promising functional tin oxide (SnOx) has attracted tremendous attention due to its transparent and conductive properties. The stoichiometric composition of SnOx can be described as common n-type SnO2 and p-type Sn3O4. In this study, the functional SnOx films were prepared successfully by plasma-enhanced atomic layer deposition (PEALD) at different substrate temperatures from 100 to 400 °C. The experimental results involving optical, structural, chemical, and electrical properties and morphologies are discussed. The SnO2 and oxygen-deficient Sn3O4 phases coexisting in PEALD SnOx films were found. The PEALD SnOx films are composed of intrinsic oxygen vacancies with O-Sn4+ bonds and then transformed into a crystalline SnO2 phase with increased substrate temperature, revealing a direct 3.5−4.0 eV band gap and 1.9−2.1 refractive index. Lower (<150 °C) and higher (>300 °C) substrate temperatures can cause precursor condensation and desorption, respectively, resulting in reduced film qualities. The proper composition ratio of O to Sn in PEALD SnOx films near an estimated 1.74 suggests the highest mobility of 12.89 cm2 V−1 s−1 at 300 °C.
Keywords: plasma-enhanced atomic layer deposition (PEALD); substrate temperature; tin oxide (SnOx).