Chronic inflammatory wounds pose therapeutic challenges in the biomedical field. Polymeric nanofibrous matrices provide extracellular-matrix-like structures to facilitate wound healing; however, wound infection and the subsequent accumulation of reactive oxygen species (ROS) delay healing. Therefore, we herein developed electrospun nanofibers (NFs), composed of chitosan-stabilized Prussian blue (PBChi) nanoparticles (NPs) and poly(vinyl alcohol) (PVA), with ROS scavenging activity to impart antioxidant and wound healing properties. The PBChi NPs were prepared using chitosan with different molecular weights, and their weight ratio with respect to PVA was optimized to yield PBChi-NP-coated PVA NFs with well-defined NF structures. In situ and in vitro antioxidant activity assays showed that the PBChi/PVA NFs could effectively remove ROS. Particularly, PBChi/PVA NFs with a lower chitosan molecular weight exhibited greater antioxidant activity. The hydroxyl radical scavenging activity of PBChi10k/PVA NFs was 60.4 %, approximately two-fold higher than that of PBChi100k/PVA NFs. Further, at the concentration of 10 μg/mL, they could significantly lower the in vitro ROS level by up to 50.7 %. The NFs caused no significant reduction in cell viability, owing to the excellent biocompatibility of PVA with PBChi NPs. Treatment using PBChi/PVA NFs led to faster cell proliferation in in vitro scratch wounds, reducing their size from 202 to 162 μm. The PBChi/PVA NFs possess notable antioxidant and cell proliferation properties as ROS-scavenging wound dressings.
Keywords: Chitosan; Electrospinning; Nanofiber; Prussian blue; Reactive oxygen species scavenging; Wound healing.
Copyright © 2022. Published by Elsevier B.V.