An appropriate amount of Zn-ions are incorporated into the high Curie temperature bismuth layer-structure ferroelectric material to fabricate Sr0.2Na0.4Pr0.4Bi4Ti4O15:xwt%ZnO; (SNPBT:xZn), with x = 0, 0.10, 0.15, and 0.20 ceramic series to investigate the magnetic, ferroelectric, and energy storage efficiency and piezoelectric properties. Pure SNPBT and SNPBT:xZn ceramics have maintained their structure even after the intercalation of Zn-ions at the lattice sites of SNPBT. The addition of ZnO in SNPBT has improved the multifunctional properties of the material at x = 0.15. At room temperature, SNPBT:0.15Zn has shown a high relative density of 96%, exhibited weak ferromagnetic behavior along with a low saturation magnetization (Ms) of 0.028 emu/g with a low coercive field of 306 Oe, a high remnant polarization (Pr) of 9.04 µC/cm2, a recoverable energy density (Wrec) of ~0.5 J/cm3, an energy conversion efficiency (η) of ~41%, a high piezoelectric co-efficient (d33) of 21 pC/N, and an impedance of 1.98 × 107 Ω, which are much improved as compared to pure SBT or pure SNPBT ceramics. Dielectric Constant (ɛr) versus temperature plots present the sharp peak for SNPBT:0.15Zn ceramic at a Curie temperature (TC) ~ 605 °C, confirming the strong ferroelectric nature of the ceramic. Moreover, SNPBT:0.15Zn ceramic has shown strong, piezoelectric, thermally stable behavior, which remains at 76% (16 pC/N) of its initial value even after annealing at 500 °C. The achieved results clearly indicate that SNPBT:0.15Zn ceramic is a promising candidate for future wide-temperature pulse power applications and high-temperature piezoelectric devices.
Keywords: SrBi4Ti4O15; ZnO; dielectric; energy storage efficiency; ferroelectric; piezoelectric.