The development of graphene conductive inks with a high conductivity and dispersion stability in water poses considerable challenges. Herein, a highly conductive Ag/carbon quantum dots (CQDs)/graphene (G) composite with good dispersity and stability in water was prepared for the first time through the in situ photoreduction of AgNO3 and deposition of Ag onto graphene nanosheets obtained via CQD-assisted liquid-phase exfoliation. Ag nanoparticles with an average size of ∼1.88 nm were uniformly dispersed on graphene nanosheets. The Ag/CQDs/G composite exhibited good dispersity and stability in water for 30 days. The formation mechanism of the Ag/CQDs/G composites was also discussed. CQDs played a vital role in coordinating with Ag+ and reducing it under visible light conditions. The addition of only 1.58 wt % of Ag NPs to the CQDs/G film resulted in a significant decrease in the electrical resistivity by approximately 89.5%, reaching a value of 0.054 Ω cm for a 40 μm thick Ag/CQDs/G film. A low resistivity of 2.15 × 10-3 Ω cm for the Ag/CQDs/G film was achieved after rolling compression with a compression ratio of 78%. The Ag/CQDs/G film exhibited good conductivity and durability when bent, rolled, or twisted. Moreover, the resistivity of the film displayed a slight deviation after 5000 bending cycles, indicating its outstanding stability. This study provides an efficient strategy for preparing graphene-based conductive composites with good dispersibility and stability in water as well as novel high-performance conductive inks for application in flexible printed electronics.
Keywords: Ag/CQDs/graphene; carbon quantum dots; conductive film; photoreduction; water-based ink.