An eco-friendly and a facile route successfully prepared novel cerium oxide nanoparticles functionalized by gelatin. The introduced CeO2@gelatin was investigated in terms of FE-SEM, EDX, TEM, chemical mapping, FT-IR, and (TGA) thermal analyses. These characterization tools indicate the successful synthesis of a material having CeO2 and gelatin as a composite material. The prepared composite CeO2@gelatin was used as an environment-friendly coated film or X60 steel alloys in acidizing oil well medium. Moreover, the effect of CeO2 percent on film composition was investigated. LPR corrosion rate, Eocp-time, EIS, and PDP tools determined the corrosion protection capacity. The CeO2@gelatin composite exhibited high protection capacity compared to pure gelatin; in particular, 5.0% CeO2@gelatin coating film shows the highest protection capacity (98.2%), with long-term anti-corrosive features. The % CeO2@gelatin-coated films formed the protective adsorbed layer on the steel interface by developing a strong bond among nitrogen atoms in the CeO2@gelatin film and the electrode interface. Surface morphology using FESEM measurements confirmed the high efficiency of the fabricated CeO2@gelatin composite on the protection X60 steel alloys. DFT calculations and MC simulations were explored to study the relations between the protection action and the molecular construction of the coated systems, which were in good alignment with the empirical findings.
Keywords: X60 steel alloys; ceria; coated films; corrosion protection; gelatin; theoretical study.