The aim of this work is to assess the influence of different commercial diluents on some mechanical properties of two bisphenolic epoxy compounds, cold-cured by a polyamide curing agent, to be employed as epoxy structural adhesives for building and industrial applications. The diluents under analysis were epoxy, bituminous, nitro, acrylic and extraction. The choice of these products was made on the basis of their wide commercial availability as diluents for epoxies used as adhesives and in different industrial and construction applications. The diluents were all added in small proportions, i.e., from 1 to 10 g per 100 g of epoxy resin. The cold-cured epoxy compounds were subjected to compressive (according to ISO 604) and static tensile (according to ISO 527-1) tests. The same mechanical tests were performed on both unmodified epoxy resins, for comparison purposes. On the basis of the obtained results, it was concluded that the influence of the presence of a diluent, and of its amount, on the mechanical properties of epoxy compounds depends on the type of resin and of diluent, as well as on the mechanical characteristics analyzed.
Keywords: diluent; epoxy resin; mechanical properties.