Titanium matrix composites (TMCs) with excellent mechanical properties, reinforced by graphene, is deemed the lightweight and high strength structural materials. In this study, TC11 titanium alloy powder and graphene nanosheets (GNPs) were used as raw materials, and the composite powder with good uniformity and fluidity was obtained through non-interventional homogeneous mixing by a planetary mixer. The microstructure and mechanical properties of the GNPs-TC11 composites and TC11 alloy were compared. The results showed that the microstructure of TC11 and the composites was acicular martensite α' phase under the process parameters of 280 W laser power, 1200 mm/s scanning speed, and 0.1 mm hatch spacing. The GNPs in addition, in the composites, reduced the acicular martensite particle size and expanded the proportion of low-angle grain boundaries. The tensile strength and percentage elongation after the fracture of the TC11 titanium alloy were 1265 MPa and 4.3%, respectively. Because of addition of the GNPs, the strength and percentage elongation after the fracture of the composite increased to 1384 MPa and 8.1%, respectively, at a GNPs mass content of 0.2%. The enhancement of mechanical properties can be attributed to grain refinement, dislocation strengthening, Orowan strengthening, and load transfer strengthening.
Keywords: GNPs/TC11 titanium matrix composite; graphene; mechanical property; microstructure; selective laser melting.