Lithium-sulfur (Li-S) batteries are promising as next-generation energy storage systems. Adsorbents for sulfide species are favorably applied to the cathode, but this substrate often results in a surface-passivating lithium sulfide(Li2 S) film with a strong adsorption of Li2 S. Here, an amorphous titanium suboxide (a-TiOx) is presented that strongly adsorbs lithium polysulfides (Li2 Sx , x < 6) but relatively weakly adsorbs to Li2 S. With these characteristics, the a-TiOx achieves high conversion of Li2 Sx and high sulfur utilization accompanying the growth of particulate Li2 S. The DFT calculations present a mechanism for particulate growth driven by the promoted diffusion and favorable clustering of Li2 S. The a-TiOx -coated carbon nanotube-assembled film (CNTF) cathode substrate cell achieves a high discharge capacity equivalent to 90% sulfur utilization at 0.2 C. The cell also delivers a high capacity of 850 mAh g-1 even at the ultra-high-speed of 10 C and also exhibits high stability of capacity loss of 0.0226% per cycle up to 500 cycles. The a-TiOx /CNTF is stacked to achieve a high loading of 7.5 mg S cm-2 , achieving a practical areal capacity of 10.1 mAh cm-2 .
Keywords: DFT calculations; amorphous titanium suboxides; high sulfur loading; lithium sulfide clustering; lithium-sulfur batteries.
© 2022 The Authors. Advanced Science published by Wiley-VCH GmbH.