Nowadays, ibuprofen and ketoprofen are widely used over-the-counter medications to treat inflammation, fever, or pain. Their high consumption and improper disposal cause them to get into the environment and often pollute surface water. In this study, the new polymeric porous microspheres based on 4-vinylpyridine (4VP) are presented as effective sorbents for ibuprofen and ketoprofen preconcentration and removal. The porous microspheres were obtained via seed swelling polymerization with the use of two types of methacrylate crosslinkers, i.e., trimethylolpropane trimethacrylate (TRIM) and 1,4-dimethacryloiloxybenzene (14DMB). Additionally, as a reference sorbent, a copolymer of styrene and divinylbenzene was obtained. Porous structure investigations showed that the microspheres possess a specific surface area of about 100 m2/g, but noticeable differences were observed in their internal topography depending on the type of crosslinker used. Moreover, the porous structure of dry and swollen microspheres differs significantly. Swollen copolymers reveal the presence of micropores. The 4VP microspheres are characterized by high thermal stability; their initial decomposition temperature is about 300 °C. The performance of the 4VP copolymers as sorbents in aqueous solutions of drugs was evaluated in static and dynamic modes at three pH values of 3, 7, and 11. The highest sorption efficiency was obtained for ibuprofen and ketoprofen in pH 3. Both 4VP copolymers indicate the high sorption capacity in a static sorption as follows: towards ketoprofen of about 40 mg/g whereas towards ibuprofen of about 90 mg/g and 75 mg/g on copolymer crosslinked with trimethylolpropane trimethacrylate and 1,4-dimethacryloiloxybenzene, respectively. The recovery of ibuprofen and ketoprofen after dynamic sorption experiments was higher than 90%.
Keywords: SPE; functional polymers; ibuprofen; ketoprofen; polymeric microspheres; porous polymers; sorption.