This in vitro study aimed to assess the erosive effect of hydrochloric acid in association with toothbrushing procedure on the surface condition of three bulk-fill composite resins used for direct restoration. A total of 480 samples (160 from each composite resin): X-tra Fil (VOCO, Germany)—group A, Filtek Bulk-fill Posterior (3M-ESPE, St. Paul, MN, USA)—group B, G-aenial Posterior (GC Japan)—group C were prepared, submitted to chemical attack for 60 min with hydrochloric acid 30% and, subsequently, submitted to the abrasive effect of toothbrushing using 10,000 cycles with medium and hard bristles, at three different times (immediately and after 30 min after acid attack or without any chemical attack). The surface roughness of the samples was measured using a noncontact profilometer (Dektak XT, Bruker, Billerica, MA, USA). The values were analyzed using ANOVA and post hoc Bonferroni tests, with a p < 0.05. Chemical attack for 60 min associated with one year of toothbrushing with toothbrushes having medium or hard bristles increase the surface roughness of tested bulk-fill composite resins. No differences were recorded between toothbrushing with medium or firm bristles immediately or 30 min after acidic challenge for each of the three bulk-fill composite resins. Exposure to hydrochloric acid determines no effect on surface roughness of bulk-fill composite resins.
Keywords: bulk-fill composite resin; hydrochloric acid; surface roughness; toothbrush.