Even though hard, low friction coatings such as diamond like carbon (DLC) would be beneficial for the performance and longevity of rubber seals, a crucial challenge remains. The elastic mismatch of rubber substrate and DLC coating prevents a fracture free coating application. In this work, a nature inspired approach is applied to render the stiff coating flexible and resilient to delamination at the same time by direct patterning. Rubber substrates were laser structured with tile patterns and subsequently DLC coated. Tensile and tribology tests were performed on structured and unstructured samples. Unstructured DLC coatings showed a crack pattern induced by the coating process, which was further fragmented by tensile stress. Coatings with tile patterns did not experience a further fragmentation under load. During continuous tribological loading, less heterogenous damage is produced for tile structured samples. The findings are ascribed to the relief of induced coating stress by the tile structure, meaning a more resilient coating.
Keywords: DLC; coating; delamination; diamond like carbon; flexible; friction; nature inspired; rubber; sealing; tribology.