In recent years, polytetrafluoroethylene (PTFE)/aluminum (Al) energetic materials with high-energy density have attracted extensive attention and have broad application prospects, but the low-energy release efficiency restricts their application. In this paper, oxide, bismuth trioxide (Bi2O3) or molybdenum trioxide (MoO3) are introduced into PTFE/Al to improve the chemical reaction performance of energetic materials. The pressurization characteristics of PTFE/Al/oxide as pressure generators are compared and analyzed. The experiments show that the significantly optimized quasi-static pressure peak, impulse, and energy release efficiency (0.162 MPa, 10.177 s·kPa, and 0.74) are achieved for PTFE/Al by adding 30 wt.% Bi2O3. On the other hand, the optimal parameter obtained by adding 10% MoO3 is 0.147 MPa, 9.184 s·kPa, and 0.68. Further, the mechanism of enhancing the energy release performance of PTFE/Al through oxide is revealed. The mechanism analysis shows that the shock-induced energy release performance of PTFE/Al energetic material is affected by the intensity of the shock wave and the chemical reaction extent of the material under the corresponding intensity. The oxide to PTFE/Al increases the intensity of the shock wave in the material, but the chemical reaction extent of the material decreases under the corresponding intensity.
Keywords: PTFE/Al/oxide; energy release performance; pressurization characteristics; shock-induced.