Polymeric nanoparticles are one method to modify the drug release of small hydrophilic molecules. In this study, clindamycin HCl was used as a model drug loaded in carboxymethyl chitosan nanoparticles cross-linked with Ca2+ ions (CMCS-Ca2+). The ultrasonication with experimental design was used to produce CMCS-Ca2+ nanoparticles loading clindamycin HCl. The model showed that the size of nanoparticles decreased when amplitude and time increased. The nanoparticle size of 318.40 ± 7.56 nm, decreased significantly from 543.63 ± 55.07 nm (p < 0.05), was obtained from 75% of amplitude and 180 s of time, which was one of the optimal conditions. The clindamycin loading content in this condition was 34.68 ± 2.54%. The drug content in nanoparticles showed an inverse relationship with the size of the nanoparticles. The sodium carboxymethylcellulose film loading clindamycin HCl nanoparticles exhibited extended release with 69.88 ± 2.03% drug release at 60 min and a gradual increase to 94.99 ± 4.70% at 24 h, and demonstrated good antibacterial activity against S. aureus and C. acne with 40.72 ± 1.23 and 48.70 ± 1.99 mm of the zone of inhibition at 24 h, respectively. Thus, CMCS-Ca2+ nanoparticles produced by the ultrasound-assisted technique could be a potential delivery system to modify the drug release of small hydrophilic antibiotics.
Keywords: carboxymethyl chitosan; clindamycin; experimental design; nanoparticle; ultrasound.