Tailoring surface carboxyl groups of mesoporous carbon boosts electrochemical H2O2 production

Abstract

Oxygen-doped porous carbon materials have been shown promising performance for electrochemical two-electron oxygen reduction reaction (2e^- ORR), an efficient approach for the safe and continuous on-site generation of H₂O₂. The regulation and mechanism understanding of active oxygen-containing functional groups (OFGs) remain great challenges. Here, OFGs modified porous carbon were prepared by thermal oxidation (MC-12-Air), HNO₃ oxidation (MC-12-HNO₃) and H₂O₂ solution hydrothermal treatment (MC-12-H₂O₂), respectively. Structural characterization showed that the oxygen doping content of three catalysts reached about 20%, with the almost completely maintained specific surface area (exception of MC-12- HNO₃). Spectroscopic characterization further revealed that hydroxyl groups are mainly introduced into MC-12-Air, while carboxyl groups are mainly introduced into MC-12- HNO₃ and MC-12- H₂O₂. Compared with the pristine catalyst, three oxygen-functionalized catalysts showed enhanced activity and H₂O₂ selectivity in 2e^- ORR. Among them, MC-12-H₂O₂ exhibited the highest catalytic activity and selectivity of 94 %, as well as a considerable HO₂^- accumulation of 46.2 mmol L^-1 and excellent stability in an extended test over 36 h in a H-cell. Electrochemical characterization demonstrated the promotion of OFGs on ORR kinetics and the greater contribution of carboxyl groups to the intrinsically catalytic activity. DFT calculations confirmed that the electrons are transferred from carboxyl groups to adjacent carbon and the enhanced adsorption strength toward *OOH intermediate, leading to a lower energy barrier for forming *OOH on carboxyl terminated carbon atoms.

Keywords: Carbon materials; Electrocatalysis; Hydrogen peroxide; Oxygen reduction reaction; Oxygen-containing functional groups.