Dispersing upconversion nanocrystals in PMMA microfiber: a novel methodology for temperature sensing

Muhammad Khuram Shahzad; Yundong Zhang; Lugui Cui; Lu Liu; Mehwish Khalid Butt; Hanyang Li

doi:10.1039/c8ra01146j

Dispersing upconversion nanocrystals in PMMA microfiber: a novel methodology for temperature sensing

RSC Adv. 2018 May 25;8(35):19362-19368. doi: 10.1039/c8ra01146j.

Authors

Muhammad Khuram Shahzad¹, Yundong Zhang¹, Lugui Cui², Lu Liu², Mehwish Khalid Butt², Hanyang Li²

Affiliations

¹ National Key Laboratory of Tunable Laser Technology, Institute of Opto-Electronics, Department of Electronics Science and Technology, Harbin Institute of Technology (HIT) Harbin 150080 China ydzhang@hit.edu.cn.
² Key Lab of In-fiber Integrated Optics, Ministry Education of China, Harbin Engineering University Harbin 150080 China hanyang_li@qq.com.

Abstract

This paper reports the synthesis of a β-NaYF₄:Yb³⁺/Tm³⁺ phosphor by a thermal decomposition method and focuses on the fabrication of microfibers by the co-doping of nanocrystals with PMMA solution via a facile drawing method. The structural characteristics of the nanocrystals are studied by XRD and TEM techniques. Meanwhile, the optical properties of the microfibers are probed by wave guiding performance and upconversion spectroscopy. With the excitation of a 980 nm laser source, the microfiber presented blue upconversion emission of Tm³⁺ ions. The fluorescence intensity ratio (FIR) method is utilized for the non-thermally coupling transition (¹D₂ → ³F₄ (452 nm) and ¹G₄ → ³H₆ (476 nm)) levels to carry out the optical thermometry. The maximum sensitivity is recorded at 298 K and is 0.00157 K^-1. The results suggest that the microfibers have potential applications in thermometry with high sensitivity.