Improvement of self-cleaning waterborne polyurethane-acrylate with cationic TiO2/reduced graphene oxide

Gang Chen; Si Ouyang; Yiqing Deng; Mengxiao Chen; Yanqing Zhao; Wangcai Zou; Qiang Zhao

doi:10.1039/c9ra03250a

Improvement of self-cleaning waterborne polyurethane-acrylate with cationic TiO₂/reduced graphene oxide

RSC Adv. 2019 Jun 13;9(32):18652-18662. doi: 10.1039/c9ra03250a. eCollection 2019 Jun 10.

Authors

Gang Chen¹, Si Ouyang¹, Yiqing Deng¹, Mengxiao Chen¹, Yanqing Zhao¹, Wangcai Zou¹, Qiang Zhao¹

Affiliation

¹ School of Chemical Engineering, Sichuan University Chengdu Sichuan 610065 P. R. China zhaoqiang@scu.edu.cn.

Abstract

UV curable waterborne polyurethane acrylate (WPUA) with surfactant-modified TiO₂/reduced graphene oxide (TiO₂/rGO) nanocomposites were prepared and analyzed to improve their mechanical performance and self-cleaning ability. TiO₂/rGO nanocomposites were prepared by a simple hydrothermal method with nano-TiO₂ and graphene oxide, and modified with cationic surfactant (CTAB) to obtain a cationic TiO₂/rGO (C-TiO₂/rGO). Then, the obtained C-TiO₂/rGO was incorporated into anionic waterborne polyurethane acrylate by in situ fabrication to obtain a composite emulsion (C-TiO₂/rGO-WPUA). The results of Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and scanning electron microscopy (SEM) showed that CTAB was successfully intercalated into TiO₂/rGO, and TiO₂ nanoparticles were evenly distributed on graphene sheets with good dispersibility. Compared to UV-cured neat WPUA and C-TiO₂/rGO-WPUA, the mechanical properties and thermal stability of the composites were significantly improved. When the content of C-TiO₂/rGO was 0.5%, the UV-cured composites had overall excellent performance. In particular, the WPUA composites exhibited good self-cleaning ability in photocatalysis. The photocatalytic degradation rate of methyl orange in 0.5% C-TiO₂/rGO-WPUA reached 88.3% under 6 h visible light irradiation.