We developed a molten salts process to prepare Co9 S8 nanoparticles (NPs) entrapped, S, N co-doped carbons. Cobalt chloride was used as the cobalt source. The melamine-formaldehyde (MF) resin provided the carbon source and nitrogen source, and thiourea provided sulfur source. In addition, common inorganic salts were added as templates to generate pores. The characterization results showed that the prepared materials contained high contents of N, S and Co, and were mesoporous composites. At the same time, the porosity of electrocatalyst depended on the type of salt and the mass ratio of precursor to salt, which further affected the electrocatalytic activity of hydrogen evolution reaction (HER). The best prepared catalyst showed excellent HER performance. The onset overpotential of the catalyst was low (33 mV) and had a small Tafel slope (61.1 mV dec-1 ), in addition to good stability in alkaline media.
Keywords: Co9S8 nanoparticle; hydrogen evolution reaction• melamine formaldehyde resin; molten salts; porous carbon.