Fibrin is widely used in vascular tissue engineering. Typically, fibrin polymerization is initiated by adding exogenous thrombin. In this study, we proposed a protocol for the preparation of completely autologous fibrin without the use of endogenous thrombin and compared the properties of the prepared fibrin matrix with that obtained by the traditional method. Fibrinogen was obtained by ethanol precipitation followed by fibrin polymerization by adding either exogenous thrombin and calcium chloride (ExThr), or only calcium chloride (EnThr). We examined the structure, mechanical properties, thrombogenicity, degradation rate and cytocompatibility of fibrin matrices. Factor XIII (FXIII) quantitative assay was performed by ELISA, and FXIII activity was assessed by SDS-PAGE detection of γ-γ cross-links. The results show that network structure of EnThr fibrin was characterized by thinner fibers. The EnThr fibrin matrices had higher strength, stiffness and resistance to proteolytic degradation compared to ExThr fibrin. EnThr fibrin matrices exhibited less thrombogenicity in vitro than ExThr, and retained high cytocompatibility. Thus, the proposed approach has several advantages over the traditional method, namely the fabrication of a completely autologous coating material that has better mechanical properties, higher resistance to proteolysis and lower thrombogenicity.
Keywords: autologous fibrin; endogenous thrombin; exogenous thrombin; fibrin matrix; vascular tissue engineering.