A biologically active agent based on a Zn-1,3,5-benzen tricarboxylic acid (Zn-BTC) framework incorporated into a chitosan (CS) biopolymer (Zn-BTC@CS) was successfully synthesized using a microwave irradiation technique. The synthesized Zn-BTC@CS was characterized using a scanning electron microscope (SEM) and the obtained data indicated a highly smooth surface morphology of the synthesized Zn-BTC and no morphological changes when the Zn-BTC covered the CS. In addition, the particle size diameter varied from 20 to 40 nm. XRD displayed a well-maintained Zn-BTC structure, and the crystal structure of Zn-BTC was not distorted by the composition of Zn-BTC and chitosan in the nanocomposite. Data from BET analysis revealed that the specific surface area of the Zn-BTC was reduced from 995.15 m2/g to 15.16 m2/g after coating with chitosan. The pore size distribution and pore volume of the Zn-BTC, Zn-BTC@CS were centered at 37.26 nm and at 22.5 nm, respectively. Zn-BTC@CS exhibited anticancer efficacy against lung and colon cancer cell lines. Zn-BTC@CS inhibited the proliferation of A549 and DLD-1 cancer cell lines in a dose-dependent manner with IC50 values of 13.2 and 19.8 µg/mL for the colon and lung cancer cell lines, respectively. Zn-BTC@CS stimulated the apoptotic process through up-regulating P53 expression and down-regulating Bcl-2 expression. Moreover, Zn-BTC@CS induced in vitro DNA fragmentation in both cancer cell lines with significantly different affinity by 66% (A549) and 20% (DLD-1) versus 52% reduction by Cisplatin. Zn-BTC@CS (IC50) exhibited anti-invasive activity and dramatically inhibited the migration of lung and colon cancer cell lines. This study provides evidence that Zn-BTC@CS targets the essential proteins involved in proliferation, metastasis, and apoptosis. Thus, Zn-BTC@CS has chemotherapeutic potential for inhibiting lung and colon cancer viability and growth.
Keywords: biological activity; biopolymer; chitosan nanocomposites; zinc–organic framework.