Polymer microspheres are important for a variety of applications, such as ion exchange chromatography, catalyst supports, absorbents, etc. Synthesis of large microspheres can be challenging, because they cannot be obtained easily via classic emulsion polymerization, but rather by more complex methods. Here, we present a facile method for obtaining polymer microspheres, beyond 50 μm, via Pickering emulsion polymerization. The method consists in creating oil-in-water (o/w) Pickering emulsion/suspension from vinyl bearing monomers, immiscible with water, whereas silica nanoparticles (NPs), bearing glycidyl functionalities, have a stabilizing role by adsorbing at the monomer/water interface of emulsion droplets. The emulsion is polymerized under UV light, and polymer microspheres decorated with NPs are obtained. We discovered that the contact angle of the NPs with the polymer microsphere is the key parameter for tuning the size and the quality of the obtained microspheres. The contact angle depends on the NPs' interfacial energy and its polar and dispersive contributions, which we determine with a newly developed NanoTraPPED method. By varying the NPs' surface functionality, we demonstrate that when their interfacial energy with water decreases, their energy of adhesion to water increases, causing the curvature of the polymer/water interface to decrease, resulting in increasingly larger polymer microspheres.
Keywords: colloidosomes; nanostructured surfaces; pickering emulsions; polymer microspheres; surface energy; wettability of nanoparticles.