The introduction of inorganic additive or nanoparticles into fluorine-free proton exchange membranes (PEMs) can improve proton conductivity and have considerable effects on the performance of polymer electrolyte membrane fuel cells. Based on the sol-gel method and in situ polycondensation, novel cross-linked PEM and nanocomposite PEMs based on a sulfonated polysulfone (SPSU) matrix were prepared by introducing graphene oxide (GO) polymeric brushes and incorporating Pt-TiO2 nanoparticles into an SPSU matrix, respectively. The results showed that the incorporation of Pt-TiO2 nanoparticles could obviously enhance self-humidifying and thermal stability. In addition, GO polymer brushes fixed on polymeric PEM by forming a cross-linked network structure could not only solve the leakage of inorganic additives during use and compatibility problem with organic polymers, but also significantly improve proton conductivity and reduce methanol permeability of the nanocomposite PEM. Proton conductivity, water uptake and methanol permeability of the nanocomposite PEM can be up to 6.93 mS cm-1, 46.58% and be as low as 1.4157 × 10-6 cm2 s-1, respectively, which represent increases of about 70%, about 22% and a decrease of about 40%, respectively, compared with that of primary SPSU. Therefore, the synergic action of the covalent cross-linking, GO polymer brush and nanoparticles can significantly and simultaneously improve the overall performance of the composite PEM.
Keywords: fuel cells; graphene oxide; nanoparticles; polymer brush; proton exchange membrane; self-humidifying; sulfonated polysulfone.