Demonstrating and Unraveling a Controlled Nanometer-Scale Expansion of the Vacancy Defects in Graphene by CO2

Abstract

A controlled manipulation of graphene edges and vacancies is desired for molecular separation, sensing and electronics applications. Unfortunately, available etching methods always lead to vacancy nucleation making it challenging to control etching. Herein, we report CO₂ -led controlled etching down to 2-3 Å per minute while completely avoiding vacancy nucleation. This makes CO₂ a unique etchant for decoupling pore nucleation and expansion. We show that CO₂ expands the steric-hindrance-free edges with an activation energy of 2.71 eV, corresponding to the energy barrier for the dissociative chemisorption of CO₂ . We demonstrate the presence of an additional configurational energy barrier for nanometer-sized vacancies resulting in a significantly slower rate of expansion. Finally, CO₂ etching is applied to map the location of the intrinsic vacancies in the polycrystalline graphene film where we show that the intrinsic vacancy defects manifest mainly as grain boundary defects where intragrain defects from oxidative etching constitute a minor population.

Keywords: CO2 Based Etching; Grain-Boundary Defects; Intrinsic Vacancy Defects; Single-Layer Graphene; Vacancy Defects; Vacancy Expansion; Vacancy Nucleation.