At present, the utilization of boron resources in China is increasing, and the problem of boron tailing pollution is becoming increasingly serious. To fundamentally solve the problem of boron tailing, many scholars at home and abroad have mainly studied the curing effect in terms of compressive strength, and little research has been carried out into the solidification effect and hydration products. This study explored the effects of adding different alcohol-based modifiers on the hydration products of magnesium oxysulfate cement-boron mud mixture, the microstructure, physical properties and curing effects of the samples. The results show that magnesium oxysulfate cement is beneficial to the solidification of boron in boron mud due to its low-alkali. Adding an alcohol-based modifier can increase the compressive strength of magnesium oxysulfate cement-boron mud blends. After adding acrylic acid and D-Mannitol, the 28-day compressive strength of the sample increased by 44.7 MPa. The blending of alcohol-based modifiers has a very good effect on the curing of boron in the whole system.
Keywords: KH550; magnesium oxysulfate cement-boron mud blends; mechanical strength; microstructure; solidification.