Filler effects on H2 permeation properties in sulfur-crosslinked ethylene propylene diene monomer (EPDM) polymers blended with two kinds of carbon black (CB) and silica fillers at different contents of 20 phr-60 phr are investigated by employing volumetric analysis in the pressure exposure range of 1.2 MPa~9.0 MPa. A linear relationship is observed between the sorbed amount and pressure for H2 gas, which is indicative of Henry's law behavior. The hydrogen solubility of EPDM composites increases linearly with increasing filler content. The magnitude of hydrogen solubility for the filled EPDM composites is dependent on the filler type. The hydrogen solubility is divided into two contributions: hydrogen absorption in the EPDM polymer and hydrogen adsorption at the filler surface. Neat EPDM reveals pressure-dependent bulk diffusion behavior. However, with increasing filler content, the diffusivity for the filled EPDM composites is found to be independent of pressure. The magnitude of filler effects on the hydrogen permeation parameter is measured in the order of high abrasion furnace CB~semireinforcing furnace CB ˃ silica, whose effect is related to the specific surface area of CB particles and interfacial structure. The correlation between the permeation parameters and filler content (or crosslink density) is discussed.
Keywords: carbon black filler; diffusion; ethylene propylene diene monomer; hydrogen uptake; permeability; silica filler; volumetric analysis.