In this study, the novel nanomaterial graphene oxide (GO) was added as a modifier to polyurethane-styrene-butadiene-styrene (SBS)-modified asphalt, and a graphene oxide/polyurethane/SBS composite-modified asphalt mix was prepared. The effect of the graphene oxide material on the low-temperature crack resistance of the asphalt and mixes was investigated by bending beam rheometer (BBR) tests, beamlet bending tests at different low temperatures, and characterization by scanning electron microscopy for its microscopic condition. OpenCV image processing was used to visually represent the low-temperature cracking of the mix. The results of the BBR tests showed that the incorporation of graphene oxide resulted in a reduction in creep stiffness S and an increase in creep rate m compared with the control asphalt. The best improvement in the low-temperature cracking resistance of the polyurethane/SBS-modified asphalt was achieved at 0.5% GO doping. The results of the small beam flexural tests showed that graphene oxide as a modifier improved the flexural strength and flexural strain of the mix, resulting in a mix with a lower stiffness modulus and a better relaxation stress capacity with the addition of graphene oxide, which is also expressed through the OpenCV images. Graphene oxide significantly improved the low-temperature crack resistance of polyurethane-SBS-modified asphalt and its mixes. As a new type of nanomaterial-modified asphalt, graphene oxide/polyurethane/SBS composite-modified asphalt shows promising applicability in cold zone roads.
Keywords: OpenCV graphics technology; graphene oxide modifier; low-temperature resistance; modified asphalt; roadworks.