In this research, we reported on the formation of highly porous foam SrTiO3/NiFe2O4 (100-xSTO/xNFO) heterostructure by joint solid-state and sol-gel auto-combustion techniques. The colloidal assembly process is discussed based on the weight ratio x (x = 0, 25, 50, 75, and 100 wt %) of NiFe2O4 in the 100-xSTO/xNFO system. We proposed a mechanism describing the highly porous framework formation involving the self-assembly of SrTiO3 due to the gelation process of the nickel ferrite. We used a series of spectrophotometric techniques, including powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), N2 adsorption isotherms method, UV-visible diffuse reflectance spectra (UV-Vis DRS), vibrating sample magnetometer (VSM), and dielectric measurements, to investigate the structural, morphological, optical, magnetic, and dielectric properties of the synthesized samples. As revealed by FE-SEM analysis and textural characteristics, SrTiO3-NiFe2O4 nanocomposite self-assembled into a porous foam with an internally well-defined porous structure. HRTEM characterization certifies the distinctive crystalline phases obtained and reveals that SrTiO3 and NiFe2O4 nanoparticles were closely connected. The specific magnetization, coercivity, and permittivity values are higher in the 75STO/25NFO heterostructure and do not decrease proportionally to the amount of non-magnetic SrTiO3 present in the composition of samples.
Keywords: heterostructure; nanocomposite; porous foam SrTiO3/NiFe2O4; sol-gel auto-combustion; solid-state reaction.