A novel type of bi-functional microencapsulated phase change material (MEPCM) microcapsules with thermal energy storage (TES) and carbon dioxide (CO2) photoreduction was designed and fabricated. The polyaniline (PANI)/titanium dioxide (TiO2)/PCN-222(Fe) hybrid shell encloses phase change material (PCM) paraffin by the facile and environment-friendly Pickering emulsion polymerization, in which TiO2 and PCN-222(Fe) nanoparticles (NPs) were used as Pickering stabilizer. Furthermore, a ternary heterojunction of PANI/(TiO2)/PCN-222(Fe) was constructed due to the tight contact of the three components on the hybrid shell. The results indicate that the maximum enthalpy of MEPCMs is 174.7 J·g-1 with encapsulation efficiency of 77.2%, and the thermal properties, chemical composition, and morphological structure were well maintained after 500 high-low temperature cycles test. Besides, the MEPCM was employed to reduce CO2 into carbon monoxide (CO) and methane (CH4) under natural light irradiation. The CO evolution rate reached up to 45.16 μmol g-1 h-1 because of the suitable band gap and efficient charge migration efficiency, which is 5.4, 11, and 62 times higher than pure PCN-222(Fe), PANI, and TiO2, respectively. Moreover, the CO evolution rate decayed inapparently after five CO2 photoreduction cycles. The as-prepared bi-functional MEPCM as the temperature regulating building materials and air purification medium will stimulate a potential application.
Keywords: CO2 photoreduction; Pickering emulsion polymerization; microencapsulated phase change material; solar thermal energy storage.