In this study, syntheses of acrylate copolymers were performed based on the monomers butyl acrylate (BA), 2-ethylhexyl acrylate (2-EHA), and acrylic acid (AA) and the second-type unsaturated photoinitiator 4-acryloyloxybenzophenone (ABP). The structure of the obtained copolymers was confirmed via FT-IR spectroscopic analysis, and the viscosity and the content of non-volatile substances were determined. The adhesive films were then coated and cross-linked using ultraviolet radiation in the UV-C range at various doses (5-50 mJ/cm2). Due to the dependence of the self-adhesive properties of the adhesive layer on the basis weight, various basis weights of the layer in the range of 30-120 g/m2 were tested. Finally, the self-adhesive properties were assessed: tack, peel adhesion, shear strength (cohesion) at 20 °C and 70 °C, as well as the SAFT test and shrinkage. The aim of the study was to determine the effect of the type of monomer used, the dose of ultraviolet radiation, and the basis weight on the self-adhesive and usable properties of the obtained self-adhesive tapes.
Keywords: UV-C crosslinking; acrylate copolymers; pressure-sensitive adhesives.