Poly (ε-caprolactone) (PCL)/hydroxyapatite (HAP) composites represent a novel material with desired properties for various applications. In this work, PCL/HAP composites at low loadings were developed through melt-extrusion processing. The effects of HAP loading on viscoelastic, thermal, structural, and mechanical properties of PCL were examined. The morphological analysis revealed better dispersion of HAP at low loadings, while aggregation was noticed at high concentrations. The complex viscosity of the prepared composites increased with increasing concentration of HAP. In addition, a significant decrease in crystallinity was observed upon increase in HAP loading. However, the elongation at break increased with increasing the concentration of HAP, probably due to a decrease in crystallinity. The onset thermal degradation temperature of PCL was enhanced at low concentrations of HAP, whereas a decrease was observed at high loading. Overall, different degrees of HAP dispersion resulted into specific property improvement.
Keywords: crystallinity; flow properties; morphology; tensile properties.