Impact of Resin Composite Viscosity and Fill-technique on Internal Gap in Class I Restorations: An OCT Evaluation

Abstract

The aim of this in vitro study was to quantitatively evaluate the internal gap of resin composites of high-and low-viscosity used in single- and incremental-fill techniques in Class I cavities exposed to thermal cycling (TC) using optical coherence tomography (OCT). Cavities of 4-mm depth and 3-mm diameter were prepared in 36 third molars randomly distributed into four groups, according to viscosity of restorative resin-based composite (high or low viscosity, all from 3M Oral Care) and technique application (bulk or incremental fill) used (n=9): RC, high-viscosity, incremental-fill, resin-based composite (Filtek Z350 XT Universal Restorative); BF, high-viscosity, bulk-fill, resin-based composite (Filtek One Bulk Fill); LRC, lowviscosity, incremental-fill, resin-based composite (Filtek Z350 XT Flowable Universal Restorative); and LBF, low-viscosity, bulk-fill, resin-based composite (Filtek Flowable Restorative). Single Bond Universal Adhesive system (3M Oral Care) was used in all the experimental groups. The incremental-fill technique was used for RC and LRC groups (2-mm increments), and a single-layer technique was used for BF and LBF groups, as recommended by the manufacturer. The internal adaptation of the resin at all dentin walls was evaluated before and after TC (5000 cycles between 5°C and 55°C) using OCT images. Five images of each restored tooth were obtained. Images were analyzed using ImageJ software that measured the entire length of the gaps at the dentin-restoration interface. The length of gaps (μm) was analyzed using two-way repeated measures ANOVA and the Tukey tests (α=0.05). There was a significant interaction between material types and TC (p=0.006), and a significant difference among all material types (p<0.0001), before and after TC (p<0.0001). Increased internal gaps at the dentin-restoration interface were noticed after TC for all groups. RC presented the lowest value of internal gap before and after TC, while LBF showed the highest values of internal gap after TC. In conclusion, TC negatively affected the integrity of internal gap, whereas high-viscosity, incremental-fill, resin-based composite presented better performance in terms of internal adaptation than low-viscosity, bulk-fill materials in Class I cavities.