Here, we discuss the applicability of (methylenebis(salicylaldehyde)-MbSA) for the fabrication of the stimuli-responsive N-carboxyethylchitosan (CEC) hydrogels with a tunable dissolution rate under physiological conditions. In comparison with non-covalent salicylimine hydrogels, MbSA cross-linking via covalent bis('imine clip') and non-covalent hydrophobic interactions allowed the fabrication of hydrogels with storage moduli > 1 kPa at ten-fold lower aldehyde/CEC molar ratio with the preservation of pH- and amino-acid responsive behavior. Although MbSA-cross-linked CEC hydrogels were stable at neutral and weakly alkaline pH, their disassembly in cell growth medium (Dulbecco's modified Eagle's medium, DMEM) under physiological conditions was feasible due to transimination reaction with amino acids contained in DMEM. Depending on the cross-linking density, the complete dissolution time of the fabricated hydrogels varied from 28 h to 11 days. The cytotoxicity of MbSA cross-linked CEC hydrogels toward a human colon carcinoma cell line (HCT 116) and primary human dermal fibroblasts (HDF) was remarkably lower in comparison with CEC-salicylimine hydrogels. Fast gelation, relatively low cytotoxicity, and tunable stimuli-induced disassembly under physiological conditions make MbSA cross-linked CEC hydrogels promising for drug encapsulation and release, 3D printing, cell culturing, and other biomedical applications.
Keywords: HCT 116; benzoic imine bond; carboxyalkylchitosan; chitosan; cytotoxicity; dynamic covalent bond; glutaraldehyde; human dermal fibroblasts; hydrogel; salicylaldehyde.