The utilization of composite materials is increasing at a growing rate in almost all types of products, due to their strength-to-stiffness ratio. From this perspective, natural waste composites, i.e., wood waste composites, have also been investigated for their effective and sustainable employment. This paper deals with the application of hard and soft wood waste (i.e., acacia and cedar wood) with epoxy resin polymer to develop high strength and thermally stable wood composites. Mechanical (tensile, flexural, impact, and hardness) and thermal properties of samples are studied using Differential Scanning Calorimeter (DSC) and Thermo Gravimetric Analysis (TGA), respectively. The properties are evaluated by varying the type of wood waste and its percentage by weight. Based on the Taguchi Orthogonal Array Mixture Design, eighteen experiments are investigated. Analysis of variance (ANOVA) results show that wood waste type and wood waste content have a significant effect on all mechanical properties. From the TGA analysis, it is predicted that both types of wood waste composites exhibit similar thermal-induced degradation profiles in terms of the initial and final degradation temperatures. From the DSC results, higher glass transition temperature Tg is detected in 10% of the hardwood waste composite, and a reducing tendency of glass transition temperature Tg is observed with exceeding wood waste content. Moreover, hardwood waste at 10% demonstrated improved decomposition temperature Td, due to strong adhesion between waste and matrix.
Keywords: differential scanning calorimeter; epoxy resin; grey relational analysis; taguchi method; thermos gravimetric analysis; wood waste.