The main objective of this study was to investigate the effects of bacterial cellulose hydrogel (BCH) incorporated into montmorillonite (MMT) and its underlying mechanisms of action on a skin wound healing mouse model following pressure injury model. Komagataeibacter hansenii was used to obtain 5 cm in diameter and 0.8 mm of thickness circular bacterial cellulose (BC) sheets, which were incorporated with MMT by deposition ex-site using a 0.1% MMT suspension (100 rpm for 24 h at 28 °C). Afterward, Fourier Transform Infrared Spectroscopy (FT-IR) and Scanning Electron Microscopy (SEM) were used to characterize the bacterial cellulose hydrogel incorporated into montmorillonite (BCH-MMT). The pressure injury model was assessed by macroscopic and histological analysis in male Swiss mice. Both, BC and BCH-MMT, showed a typical FTIR spectrum of cellulosic substrates with pronounces bands around 3344, 2920, 1637, and 1041 cm-1 while microparticles of MMT dispersed uniformly throughout BC were revealed by SEM photographs. Animals treated with BCH-MMT showed significant healing of pressure ulcers as demonstrated by reduced area of redness and spontaneous hyperalgesia, lower amounts of in-site inflammatory cells (to the same level as the positive control Dersani®) and ultimately, complete epidermis re-epithelialization and tissue regeneration. Altogether, these findings suggest that a modified BCH-MMT film could serve as scaffolding for skin tissue engineering and potentially as a novel dressing material for pressure injury.
Keywords: Bacterial cellulose; Montmorillonite; Tissue regeneration.
Copyright © 2021. Published by Elsevier B.V.