In this paper, the reinforcement of concrete combining composite materials with carbon, glass and aramid fibers is discussed. Accordingly, cement specimens reinforced with chopped carbon fibers were manufactured via the retrofitting method and coated using various different types of fabrics (carbon, glass and aramid), and epoxy resin systems were developed and studied using compressive strength tests. In addition, polymeric matrix (epoxy resin) composite materials reinforced with different types of fabric (carbon, glass and aramid (Kevlar® 49)) were manufactured and their shear and bending strengths were measured. Before reinforcing cement specimens, all fabrics (carbon, glass and aramid (Kevlar® 49)) were placed in a vacuum chamber and were processed via pre-impregnation. This specific reinforcing method significantly improved the mechanical properties of cementitious structures with compressive strength values that reached 81 MPa. In a similar way, the bending and shear strengths of the materials under study were measured at 405 MPa and 33 MPa, respectively.
Keywords: Kevlar® 49; carbon fibers; composite materials; glass fiber; reinforced concrete.