The modification of poly (l-lactic acid) (PLLA) electrospun nanofibrous scaffolds was carried out by blending with second-generation poly amidoamine (PAMAM) for enhancement of their ionic conductivity. The samples containing PLLA and various amounts of PAMAM (1%, 3%, 5%, and 7% by wt.) were fabricated by electrospinning techniques. The electrospun fibers were characterized using scanning electron microscopy (SEM), porosity, Fourier-transform infrared (FTIR) spectroscopy, differential scanning calorimetry, contact angle measurement, water uptake measurement, mechanical properties, and electrical properties. Furthermore,in vitrodegradation study and cell viability assay were investigated in biomaterial applications. Creating amide groups through aminolysis reaction was confirmed by FTIR analysis successfully. The results reveal that adding PAMAM caused an increase in fiber diameter, crystallinity percentage, hydrophilicity, water absorption, elongation-at-break, and OE-mesenchymal stem cell viability. It is worth mentioning that this is the first report investigating the conductivity of PLLA/PAMAM nanofiber. The results revealed that by increasing the amount of PAMAM, the ionic conductivity of scaffolds was enhanced by about nine times. Moreover, the outcomes indicated that the presence of PAMAM could improve the limitations of PLLA like hydrophobicity, lack of active group, and poor cell adhesion.
Keywords: PAMAM dendrimer; ionic conductivity; poly (l-lactic acid).
© 2021 IOP Publishing Ltd.