The prevention of root fractures of pulpless teeth is an important clinical issue to maintain healthy teeth through lifetime. The aim of this study was to examine a clinically effective treatment method for strengthening vulnerable pulpless teeth using CAD/CAM (computer-aided design/computer-aided manufacturing) fiber-reinforced post-core by conducting a fracture resistance test. A post-core made with a fiber-reinforced resin disk TRINIA (TR, SHOFU, Kyoto, Japan) was fabricated using a CAD/CAM system. The fiber-layer orientation of the CAD/CAM post-core was parallel to the axis of the restored tooth. A post-core using a conventional composite and a fiber post (CF) was also prepared. A fracture resistance test of teeth restored with the post-cores and zirconia crowns was conducted using a universal testing machine, and fracture patterns were identified by micro-CT observation. The fracture load of the roots restored with TR was 1555.9 ± 231.8 N, whereas that of CF was 1082.1 ± 226.7 N. The fracture load of TR was 43.8% that was significantly higher than that of CF (Student's t-test, p < 0.05). The restored teeth with CAD/CAM resin post-core were found to be repairable even after fracture. These results suggest that the CAD/CAM indirect fiber post-core has the potential to strengthen the vulnerable pulpless teeth.
Keywords: CAD/CAM; fiber-reinforced resin composites; indirect post-core.