Ultrahigh molecular weight polyethylene (UHMWPE) materials have been prevalent joint replacement materials for more than 45 years because of their excellent biocompatibility and wear resistance. In this study, functionalized activated nanocarbon (FANC) was prepared by grafting maleic anhydride polyethylene onto acid-treated activated nanocarbon. A novel porous UHMWPE composite was prepared by incorporating the appropriate amount of FANC and pore-forming agents during the hot-pressing process for medical UHMWPE powder. The experimental results showed that the best prepared porous UHMWPE/FANC exhibited appropriate tensile strength, porosity, and excellent hydrophilicity, with a contact angle of 65.9°. In vitro experiments showed that the porous UHMWPE/FANC had excellent biocompatibility, which is due to its porous structure and hydrophilicity caused by FANC. This study demonstrates the potential viability for our porous UHMWPE/FANC to be used as cartilage replacement material for biomedical applications.
Keywords: activated nanocarbon; biocompatibility in vitro; hydrophilicity; porous materials.