A TiO2/ZnO oxide system was proposed as a support for the immobilization of laccase from Trametes versicolor (LTV). The obtained TiO2/ZnO/LTV biocatalytic system was then applied in the decolorization/degradation of C.I. Reactive Black 5 and C.I. Acid Green 25 dyes. The efficiency of immobilization was evaluated based on catalytic properties (Bradford method, oxidation reaction of 2,2-azino-bis(3-ethylbenzothiazoline-6-sulfonic acid)) and physicochemical (spectroscopic, porous, electrokinetic) analysis. The immobilization process was carried out with high performance (99.4%). Immobilized laccase retained about 40% of its activity in the whole analyzed temperature range and after 10 reaction cycles. Immobilization efficiency was also indirectly confirmed by the presence of characteristic functional groups (-C-H and -C-O), nitrogen and carbon on the TiO2/ZnO/LTV biocatalytic surface, identified by spectroscopic analyses. The increase in the surface area to 126 m2/g, change of isoelectric point (2.0) and zeta potential ranges (from +12.0 to -20.0 mV) after the immobilization process were also observed. The results show that the designed biocatalytic system enables the removal of acid dyes (C.I. Reactive Black 5 and C.I. Acid Green 25) with high efficiency (99% and 70%, respectively). Mass spectroscopy analysis indicated possible degradation products formed by the cleavage of N=N and C-N bonds.
Keywords: azo and anthraquinone dyes; decolorization; immobilization; laccase from Trametes versicolor; titania; zinc oxide.