In this study, Ti-6Al-4V alloy samples were processed by micro-arc oxidation (MAO) in phytic acid (H12Phy) electrolytes with the addition of different concentrations of EDTA-MgNa2 (Na2MgY) and potassium hydroxide (KOH). The surface characterization and cytocompatibility of MAO-treated samples were evaluated systematically. H12Phy is a necessary agent for MAO coating formation, and the addition of Na2MgY and KOH into the electrolytes increases the surface roughness, micropore size and Mg contents in the coatings. The MAO coatings are primarily composed of anatase, rutile, MgO and Mg3(PO4)2. Magnesium (Mg) ions in the electrolytes enter into MAO coatings by diffusion and electromigration. The MAO coatings containing 2.97 at% Mg show excellent cell viability, adhesion, proliferation, alkaline phosphatase activity, extracellular matrix (ECM) mineralization and collagen secretion, but the cytocompatibility of the MAO coatings containing 6.82 at% Mg was the worst due to the excessively high Mg content. Our results revealed that MAO coatings with proper Mg contents improve the cytocompatibility of the Ti-6Al-4V alloys and have large potential in orthopedic applications.
Keywords: H12Phy; cytocompatibility; magnesium; micro-arc oxidation; titanium alloys.