Clinical trials conducted in many centres worldwide indicate that, despite advances made in the use of biomaterials for medical applications, tribocorrosive wear remains a significant issue. The release of wear residue into body fluids can cause inflammation and, as a result, implant failure. Surface modification is one of the methods used to improve the mechanical, tribological, and fatigue properties of biomaterials. In this article, the authors investigated the impact of ion implantation on improving the functional properties of implant surfaces. This paper presents morphology, geometric surface structure, hardness, and tribological test results for layers obtained by ion implantation with nitrogen and oxygen ions on alloy 316L. The surface morphology and thickness of the implanted layer were examined using scanning microscopy. Atomic force microscopy was used to evaluate the geometric structure of the surface. Instrumented indentation was used to measure nanohardness. Model tribo tests were carried out for reciprocating motion under conditions of dry friction and lubricated friction with Ringer's solution. The tribological tests showed that the implanted samples had a lower wear than the reference samples. Nitrogen ion implantation increased the hardness of 316L steel by about 45% and increased it by about 15% when oxygen ions were used.
Keywords: biomaterials; friction; hardness; ion implantation; wear.