The mild hydrotreatment of a model mixture of tar-type compounds (i.e., naphthalene, 1-methylnaphthalene, acenaphthylene, and phenanthrene) to produce partially hydrogenated products in the range of C9-C15 was studied over Pd supported on TiO2 possessing different crystalline phases. Pd-based catalysts were prepared and characterized by ICP analysis, XRD, N2 adsorption isotherms, HR-TEM, and NH3-TPD, among others. The hydrotreatment activity and selectivity towards the desired hydrogenated products (i.e., tetralin and others) increased with both the acidity and surface area of the catalyst, along with the presence of small and well distributed Pd nanoparticles. For the selected 1.3 wt% Pd/TiO2 nano catalyst, the operational conditions for maximizing tar conversion were found to be 275 °C, 30 bar of H2, and 0.2 g of catalyst for 7 h. The catalyst revealed remarkable hydrotreatment activity and stability after several reuses with practically no changes in TiO2 structure, quite low carbon deposition, and any Pd leaching detected, thus maintaining both a small Pd particle size and adequate distribution, even after regeneration of the catalyst. Additionally, the Pd/TiO2 nano catalyst was demonstrated to be more active than other commonly used metal/alumina and more selective than metal/USY zeolites in the mild hydrotreatment of tar-type compounds, thus providing an efficient catalytic route for obtaining partially hydrogenated C9-C15 hydrocarbons useful as jet-fuel components or additives (improvers), as well as chemicals and solvents for industrial applications.
Keywords: Pd catalyst; Pd on titania; metal supported; mild hydrotreatment; tars.