Currently, cellulose acetate (CA) membranes dominate membrane-based CO2 separation for natural gas purification due to their economical and green nature. However, their lower CO2 permeability and ease of plasticization are the drawbacks. To overcome these weaknesses, we have developed high-performance mixed matrix membranes (MMMs) consisting of cellulose triacetate (CTA), cellulose diacetate (CDA), and amine functionalized zeolitic imidazolate frameworks (NH2-ZIF-8) for CO2 separation. The NH2-ZIF-8 was chosen as a filler because (1) its pore size is between the kinetic diameters of CO2 and CH4 and (2) the NH2 groups attached on the surface of NH2-ZIF-8 have good affinity with CO2 molecules. The incorporation of NH2-ZIF-8 in the CTA/CDA blend matrix improved both the gas separation performance and plasticization resistance. The optimized membrane containing 15 wt.% of NH2-ZIF-8 had a CO2 permeability of 11.33 Barrer at 35 °C under the trans-membrane pressure of 5 bar. This is 2-fold higher than the pristine membrane, while showing a superior CO2/CH4 selectivity of 33. In addition, the former had 106% higher CO2 plasticization resistance of up to about 21 bar and an impressive mixed gas CO2/CH4 selectivity of about 40. Therefore, the newly fabricated MMMs based on the CTA/CDA blend may have great potential for CO2 separation in the natural gas industry.
Keywords: CO2 separation; mixed matrix membrane; plasticization resistance; polymer blend; zeolitic imidazolate frameworks.