A new expandable graphite (EG) type was studied as a flame retardant additive in Polyamide 6 (PA6). The fire behavior was characterized by a cone calorimeter using external heat fluxes of 35, 50 and 65 kW/m2, limiting the oxygen index (LOI) and UL-94 burning tests. Additionally, electric and thermal conductivity as well as rheological properties were characterized to provide a general property overview. Fire tests were conducted using dry and humid conditioned samples. Cone Calorimeter tests showed a minimum filling degree of 15 wt.% (8.6 vol.%) EG was required to achieve a significant fire inhibiting effect in PA6 independent of the sample condition. UL-94 fire tests show a V0 classification at filling degrees greater than 20 wt.% (humid) and 25 wt.% (dry), although the associated LOI values of 39% and 38% demonstrate good flammability inhibition. Correlation analyses were conducted to identify major influences given by the sample condition for most important key figures measured in cone calorimeter tests. Accordingly, humid-conditioned samples containing between 2.5 (PA6 + 25 wt.% EG) and 4.2 wt.% (PA6) water were found to reduce the total heat evolved (THE) on average by 16% and the total smoke production (TSP) on average by 22%.
Keywords: PA6; electrical conductivity; expandable graphite; flame retardant; rheological properties; sample conditioning; thermal conductivity.